A621DQ-SAE1010 steel

ASTM-SAE A621DQ-SAE1010 steel plate/sheet,ASTM-SAE A621DQ-SAE1010 steel plate/sheet, under ASTM standard, we can regard A621DQ-SAE1010 steel plate/sheet as stamping and cold forming steels.ASTM-SAE A621DQ-SAE1010 is mainly used as stamping and cold forming steels.


ASTM-SAE A621DQ-SAE1010 carbon steels at room temperature (25°C) ranges from 190 to 210 GPa. The typical density of carbon steels is about 7.85 g/cm3. The wide range of ultimate tensile strength is largely due to different heat treatment conditions of ASTM-SAE A621DQ-SAE1010 .Other designations of ASTM-SAE A621DQ-SAE1010 carbon steel can  also be found.
 

ASTM-SAE A621DQ-SAE1010 steel plate/sheet is stamping and cold forming steels,which is according to ASTM-SAE standard,and based on the different thickness,the tensile strength of A621DQ-SAE1010 is 440MPa.The ASTM-SAE A621DQ-SAE1010 is equivalent to DIN1614:STW22, JISG3131:SPHD,EN10111 DD11,UNI5867:FEP11, NFA36-301:1C,BS1449:HR3 and UNE36.093:AP11 steels.

A621DQ-SAE1010 ASTM-SAE Number: 1.0332 Comparison of steel grades
UNI5867 FEP11
DIN1614 STW22
NFA 36-301 1C
JIS G 3131 SPHD
 EN 10111 DD11
BS1449 HR3
UNE36.093 AP11

ASTM-SAE A621DQ-SAE1010 steel plate/sheet Chemical analysis -% by mass*

Chemical elements C Si 
max
Mn max P
max.
S
max.
DD11 0.12 -- 0.60 0.045 0.045

 ASTM-SAE A621DQ-SAE1010 steel plate/sheet Mechanical properties 

thickness Yield Strength ReH 
[N/mm2] transv.min.
Tensile Strength Rm 
[N/mm2] transv.
Fracture Elongation
[%]transv. min.
Bending Test transv.
bending mandrel Ø 
angle = 180° s = plate 
thickness
t≤ 16mm t >16mm 170-340     1 S
   t < 3mm    t ≥ 3mm   440  
Up to 1.5mm 1.51-2.00mm 2.01-2.50mm 2.51-2.99mm   ≥ 3mm     23 A80 24 A80 28 A5